Polymerizable compound, polymerizable composition, polymer, and optically anisotropic product

ABSTRACT

A compound represented by a formula (IIa) is provided. In formula (IIa), Y 1  to Y 8  represent —O—, —S—, —O—C(═O)—, —C(═O)—O— or the like, G 1  and G 2  represent a divalent linear aliphatic group having 1 to 20 carbon atoms or the like, Z 1  and Z 2  represent an alkenyl group having 2 to 10 carbon atoms or the like, A x  represents a group represented by a formula (II), wherein X represents an oxygen atom, a sulfur atom or the like, D represents an alkylene group having 1 to 20 carbon atoms or the like, A 1  represents a trivalent aromatic group or the like, A 2  and A 3  represent a divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms or the like, A 4  and A 5  represent a divalent aromatic group having 4 to 30 carbon atoms or the like, Q 1  represents an alkyl group having 1 to 6 carbon atoms or the like, and m and n are 0 or 1.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. application Ser. No. 15/032,120 filed Apr. 26, 2016, which is a National Stage Application of PCT/JP2014/078920 filed Oct. 30, 2014, which claims priority based on Japanese Patent Application No. 2013-227642 filed Oct. 31, 2013. The disclosures of the prior applications are hereby incorporated by reference herein in their entirety.

TECHNICAL FIELD

The present invention relates to a polymerizable compound, a polymerizable composition, and a polymer that can produce an optical film that achieves uniform conversion of polarized light over a wide wavelength band, and does not show a change in wavelength dispersion even when the dose of ultraviolet rays applied to effect curing is increased, and also relates to an optically anisotropic product.

BACKGROUND ART

A flat panel display (FPD) that utilizes an optical film (e.g., polarizer and retardation film) can achieve high-resolution display, and has been widely used as a display device that exhibits excellent performance.

A quarter-wave plate that converts linearly polarized light into circularly polarized light, a half-wave plate that changes the plane of vibration of linearly polarized light by 900, and the like are known. Such a retardation film can achieve accurate conversion of specific monochromatic light so that ¼λ or ½λ retardation occurs.

However, a known retardation film has a problem in that polarized light that passes through is converted into colored polarized light. Specifically, since a material that forms the retardation film has wavelength dispersion with respect to retardation, and a polarization state distribution corresponding to each wavelength occurs with respect to white light that includes different light rays in the visible region, it is impossible to achieve accurate 1/4λ or ½λ retardation over the entire wavelength band.

In order to solve the above problem, various types of wideband retardation films that can achieve uniform retardation with respect to light over a wide wavelength band (i.e., retardation films having reverse wavelength dispersion) have been studied (see Patent Literature 1 to 6, for example).

It has been desired to reduce the thickness of a flat panel display as much as possible along with an improvement in performance and widespread use of mobile information terminals (e.g., mobile personal computers and mobile phones). Therefore, a reduction in thickness of the retardation film has also been desired.

It has been considered that it is most effective to produce a retardation film by applying a polymerizable composition that includes a low-molecular-weight polymerizable compound to a film substrate in order to reduce the thickness of the retardation film. Various low-molecular-weight polymerizable compounds having excellent wavelength dispersion, and various polymerizable compositions using such polymerizable compounds have been developed (see Patent Literature 7 to 24, for example).

However, the low-molecular-weight polymerizable compounds or the polymerizable compositions disclosed in Patent Literature 7 to 24 have a number of problems in that reverse wavelength dispersion may be insufficient, or it may be difficult to apply the low-molecular-weight polymerizable compounds or the polymerizable compositions to a film due to a high melting point that is not suitable for an industrial process, or the temperature range in which liquid crystallinity is obtained may be very narrow, or solubility in a solvent generally used for an industrial process may be low. Moreover, since these low-molecular-weight polymerizable compounds and the like are synthesized by performing a plurality of steps using a synthesis method that utilizes an expensive reagent, the production cost increases.

A novel polymerizable hydrazone compound and a novel polymerizable azine compound have been proposed as a liquid crystal material that may solve these problems (see Patent Literature 25 to 30).

However, when the polymerizable azine compound is applied, dried, subjected to an alignment treatment, and photo-cured using ultraviolet rays to form a polymer film, a change in wavelength dispersion may occur depending on the dose of ultraviolet rays. Specifically, when the polymerizable azine compound is used, reverse wavelength dispersion may be lost (i.e., normal wavelength dispersion may be obtained) when the dose of ultraviolet rays applied to effect curing is increased.

CITATION LIST Patent Literature

Patent Literature 1: JP-A-10-68816

Patent Literature 2: JP-A-10-90521

Patent Literature 3: JP-A-11-52131

Patent Literature 4: JP-A-2000-284126 (US20020159005A1)

Patent Literature 5: JP-A-2001-4837

Patent Literature 6: WO2000/026705

Patent Literature 7: JP-A-2002-267838

Patent Literature 8: JP-A-2003-160540 (US20030102458A1)

Patent Literature 9: JP-A-2005-208414

Patent Literature 10: JP-A-2005-208415

Patent Literature 11: JP-A-2005-208416

Patent Literature 12: JP-A-2005-289980 (US20070176145A1)

Patent Literature 13: JP-A-2006-330710 (US20090072194A1)

Patent Literature 14: JP-A-2009-179563 (US20090189120A1)

Patent Literature 15: JP-A-2010-31223

Patent Literature 16: JP-A-2011-6360

Patent Literature 17: JP-A-2011-6361

Patent Literature 18: JP-A-2011-42606

Patent Literature 19: JP-T-2010-537954 (US20100201920A1)

Patent Literature 20: JP-T-2010-537955 (US20100301271A1)

Patent Literature 21: WO2006/052001 (US20070298191A1)

Patent Literature 22: U.S. Pat. No. 6,139,771

Patent Literature 23: U.S. Pat. No. 6,203,724

Patent Literature 24: U.S. Pat. No. 5,567,349

Patent Literature 25: JP-A-2012-141245

Patent Literature 26: JP-A-2012-147904

Patent Literature 27: Japanese Patent Application No. 2012-232315

Patent Literature 28: Japanese Patent Application No. 2013-075379

Patent Literature 29: Japanese Patent Application No. 2013-027240

Patent Literature 30: Japanese Patent Application No. 2013-075379

SUMMARY OF INVENTION Technical Problem

The invention was conceived in view of the above situation. An object of the invention is to provide a polymerizable compound, a polymerizable composition, and a polymer that have a practical low melting point, exhibit excellent solubility in a general-purpose solvent, can be produced at low cost, and can produce an optical film that achieves uniform conversion of polarized light over a wide wavelength band, and does not show a change in wavelength dispersion even when the dose of ultraviolet rays applied to effect curing is increased, and an optically anisotropic product.

Solution to Problem

The inventors conducted extensive studies in order to solve the above problem. As a result, the inventors found that a polymerizable compound represented by the following formula (I), a polymerizable composition that includes the polymerizable compound and an initiator, and a polymer obtained by polymerizing the polymerizable compound or the polymerizable composition have a practical low melting point, exhibit excellent solubility in a general-purpose solvent, can be produced at low cost, and can produce an optically anisotropic product that achieves uniform conversion of polarized light over a wide wavelength band, and does not show a change in wavelength dispersion even when the dose of ultraviolet rays applied to effect curing is increased. This finding has led to the completion of the invention.

Several aspects of the invention provide the following polymerizable compound (see (1) to (7)), polymerizable composition (see (8) and (9)), polymer (see (10) and (11)), and optically anisotropic product (see (12)).

(1) A polymerizable compound represented by the following formula (I),

wherein each of Y¹ to Y⁹ independently represents a chemical single bond, —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR¹—C(═O)—, —C(═O)—NR—, —O—C(═O)—NR—, —NR¹—C(═O)—O—, —NR¹—C(═O)—NR—, —O—NR—, or —NR¹—O—, R¹ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, each of G¹ and G² independently represents a substituted or unsubstituted divalent linear aliphatic group having 1 to 20 carbon atoms, each of Z¹, Z², and Z³ independently represents an alkenyl group having 2 to 10 carbon atoms that is substituted with a halogen atom, or unsubstituted, A^(x) represents a group represented by the following formula (II),

wherein X represents —NR²—, an oxygen atom, a sulfur atom, —SO—, or —SO₂—, and R² represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, provided that an arbitrary C—H is optionally substituted with a nitrogen atom,

D represents a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR³—C(═O)—, —C(═O)—NR³—, —NR³—, or —C(═O)—, or a substituted or unsubstituted cycloalkanediyl group having 3 to 20 carbon atoms, provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded, and R³ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms,

-   -   A¹ represents a substituted or unsubstituted trivalent aromatic         group,

each of A² and A³ independently represents a substituted or unsubstituted divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms,

each of A⁴ and A⁵ independently represents a substituted or unsubstituted divalent aromatic group having 4 to 30 carbon atoms,

-   -   Q¹ represents a hydrogen atom, or a substituted or unsubstituted         alkyl group having 1 to 6 carbon atoms, and m and n are         independently 0 or 1.

(2) The polymerizable compound according to (1), wherein D is a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, or —C(═O)—, provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded.

(3) The polymerizable compound according to (1), wherein A¹ is a substituted or unsubstituted trivalent benzene ring group, or a substituted or unsubstituted trivalent naphthalene ring group.

(4) The polymerizable compound according to (1), wherein each of Y¹ to Y⁹ is independently a chemical single bond, —O—, —O—C(═O)—, —C(═O)—O—, or —O—C(═O)—O—.

(5) The polymerizable compound according to (1), wherein each of Z¹, Z², and Z³ is independently CH₂═CH—, CH₂═C(CH₃)—, or CH₂═C(Cl)—.

(6) The polymerizable compound according to (1), wherein each of G¹ and G² is independently a substituted or unsubstituted divalent aliphatic group having 1 to 12 carbon atoms that optionally includes —O—, —O—C(═O)—, —C(═O)—O—, or —C(═O)—, provided that a case where the aliphatic group includes two or more contiguous —O— is excluded.

(7) The polymerizable compound according to (1), wherein each of G¹ and G² is independently an alkylene group having 1 to 12 carbon atoms.

(8) A polymerizable composition including at least one type of the polymerizable compound according to any one of (1) to (7).

(9) A polymerizable composition including at least one type of the polymerizable compound according to any one of (1) to (7), and an initiator.

(10) A polymer obtained by polymerizing the polymerizable compound according to any one of (1) to (7), or polymerizing the polymerizable composition according to (8) or (9).

(11) The polymer according to (10), the polymer being a liquid crystal polymer.

(12) An optically anisotropic product including the polymer according to (11).

Advantageous Effects of Invention

The polymerizable compound, the polymerizable composition, and the polymer according to the aspects of the invention can inexpensively produce an optically anisotropic product that achieves uniform conversion of polarized light over a wide wavelength band, and does not show a change in wavelength dispersion even when the dose of ultraviolet rays applied to effect curing is increased (i.e., exhibits satisfactory performance).

Since the optically anisotropic product according to one aspect of the invention is produced using the polymerizable compound, the polymerizable composition, or the polymer according to one aspect of the invention, the optically anisotropic product can be produced at low cost, can achieve uniform conversion of polarized light over a wide wavelength band, and exhibits satisfactory performance. In particular, the optically anisotropic product according to one aspect of the invention does not show a change in wavelength dispersion even when the dose of ultraviolet rays applied to effect curing is changed during the production process. Specifically, it is possible to increase the degree of freedom with regard to the production process.

An antireflective film may be produced by combining the film-like optically anisotropic product according to one aspect of the invention with a polarizer. The antireflective film may suitably be used as an antireflective film for a touch panel or an organic electroluminescence device, for example.

DESCRIPTION OF EMBODIMENTS

A polymerizable compound, a polymerizable composition, a polymer, and an optically anisotropic product according to the exemplary embodiments of the invention are described in detail below.

1) Polymerizable Compound

A polymerizable compound according to one embodiment of the invention is a compound represented by the formula (I).

each of Y¹ to Y⁹ in the formula (I) independently represents a chemical single bond, —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR¹—C(═O)—, —C(═O)—NR¹—, —O—C(═O)—NR¹—, —NR¹—C(═O)—O—, —NR¹—C(═O)—NR¹—, —O—NR¹—, or —NR¹—O—.

R¹ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms.

Examples of the alkyl group having 1 to 6 carbon atoms that may be represented by R¹ include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, a sec-butyl group, a t-butyl group, an n-pentyl group, an n-hexyl group, and the like.

R¹ is preferably a hydrogen atom or an alkyl group having 1 to 4 carbon atoms.

It is preferable that Y¹ to Y⁹ included in the polymerizable compound according to one embodiment of the invention be independently a chemical single bond, —O—, —O—C(═O)—, —C(═O)—O—, or —O—C(═O)—O—.

Each of G¹ and G² independently represents a substituted or unsubstituted divalent linear aliphatic group having 1 to 20 carbon atoms. Note that the expression “substituted or unsubstituted” used herein in connection with a group or the like means that the group or the like is unsubstituted, or substituted with a substituent (hereinafter the same).

Examples of the divalent linear aliphatic group having 1 to 20 carbon atoms include an alkylene group having 1 to 20 carbon atoms, such as a methylene group, an ethylene group, a trimethylene group, a propylene group, a tetramethylene group, a pentamethylene group, a hexamethylene group, an octamethylene group, and a decamethylene group (—(CH₂)₁₀—); an alkenylene group having 2 to 20 carbon atoms, such as a vinylene group, a 1-methylvinylene group, a propenylene group, a 1-butenylene group, a 2-butenylene group, a 1-pentenylene group, and a 2-pentenylene group; and the like.

Examples of a substituent that may substitute the divalent linear aliphatic group represented by G₁ and G₂ include a halogen atom such as a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom; an alkoxy group having 1 to 6 carbon atoms, such as a methoxy group, an ethoxy group, an n-propoxy group, an isopropoxy group, an n-butoxy group, a sec-butoxy group, a t-butoxy group, an n-pentyloxy group, and an n-hexyloxy group; and the like. Among these, a fluorine atom, a methoxy group, and an ethoxy group are preferable.

The linear aliphatic group optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR²—C(═O)—, —C(═O)—NR²—, —NR²—, or —C(═O)—. Note that a case where the linear aliphatic group includes two or more contiguous —O— or —S— is excluded. R² is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms same as that represented by R¹, and is preferably a hydrogen atom or a methyl group.

—O—, —O—C(═O)—, —C(═O)—O—, and —C(═O)— are preferable as the group that is optionally included in the linear aliphatic group.

Specific examples of the linear aliphatic group that includes the above group include —CH₂—CH₂—O—CH₂—CH₂—, —CH₂—CH₂—S—CH₂—CH₂—, —CH₂—CH₂—O—C(═O)—CH₂—CH₂—, —CH₂—CH₂—C(═O)—O—CH₂—CH₂—, —CH₂—CH₂—C(═O)—O—CH₂—, —CH₂—O—C(═O)—O—CH₂—CH₂—, —CH₂—CH₂—NR²—C(═O)—CH₂—CH₂—, —CH₂—CH₂—C(═O)—NR²—CH₂—, —CH₂—NR²—CH₂—CH₂—, —CH₂—C(═O)—CH₂—, and the like.

It is preferable that each of G¹ and G² be independently a substituted or unsubstituted divalent linear aliphatic group having 1 to 12 carbon atoms that optionally includes —O—, —O—C(═O)—, —C(═O)—O—, or —C(═O)—, provided that a case where the aliphatic group includes two or more contiguous —O— is excluded. It is more preferable that each of G¹ and G² be independently a divalent linear aliphatic group such as an alkylene group having 1 to 12 carbon atoms or an alkenylene group having 2 to 20 carbon atoms, still more preferably an alkylene group having 1 to 12 carbon atoms, and particularly preferably a tetramethylene group (—(CH₂)₄—), a hexamethylene group (—(CH₂)₆—), an octamethylene group (—(CH₂)₈—), or a decamethylene group (—(CH₂)₁₀—).

Each of Z¹ to Z³ independently represents an alkenyl group having 2 to 10 carbon atoms that is substituted with a halogen atom, or unsubstituted. The number of carbon atoms of the alkenyl group is preferably 2 to 6.

Examples of the halogen atom that may substitute the alkenyl group represented by Z¹ and Z² include a fluorine atom, a chlorine atom, a bromine atom, and the like. Among these, a chlorine atom is preferable.

Specific examples of the alkenyl group having 2 to 10 carbon atoms represented by Z¹ to Z³ include CH₂═CH—, CH₂═C(CH₃)—, CH₂═CH—CH₂—, CH₃—CH═CH—, CH₂═CH—CH₂CH₂—, CH₂═C(CH₃)—CH₂CH₂—, (CH₃)₂C═CH—CH₂—, (CH₃)₂C═CH—CH₂CH₂—, CH₂═C(Cl)—, CH₂═C(CH₃)—CH₂—, CH₃—CH═CH—CH₂—, and the like.

It is preferable that each of Z¹ to Z³ be independently CH₂═CH—, CH₂═C(CH₃)—, CH₂═C(Cl)—, CH₂═CH—CH₂—, CH₂═C(CH₃)—CH₂—, or CH₂═C(CH₃)—CH₂CH₂—, more preferably CH₂═CH—, CH₂═C(CH₃)—, or CH₂═C(Cl)—, and particularly preferably CH₂═CH—, in order to more advantageously achieve the intended effects of the invention.

A^(x) represents a group represented by the following formula (II). Note that the symbol “-” in the formula (II) represents a bond from the ring (hereinafter the same).

wherein X represents —NR²—, an oxygen atom, a sulfur atom, —SO—, or —SO₂—, and R² represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms same as that represented by R¹.

An arbitrary C—H included in the group represented by the formula (II) is optionally substituted with a nitrogen atom. Examples of the group represented by the formula (II) in which an arbitrary C—H is substituted with a nitrogen atom include groups respectively represented by the following formulas.

A^(x) is preferably a group among groups respectively represented by the following formulas.

A^(x) is particularly preferably the group represented by the following formula.

D represents a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms, or a substituted or unsubstituted cycloalkanediyl group having 3 to 20 carbon atoms.

The alkylene group having 1 to 20 carbon atoms optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR³—C(═O)—, —C(═O)—NR³—, —NR³—, or —C(═O)—. Note that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded.

R³ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms same as that represented by R¹.

Examples of the alkylene group having 1 to 20 carbon atoms (that is substituted or unsubstituted) that may be represented by D include a methylene group, an ethylene group, an n-propylene group, an isopropylene group, an n-butylene group, an isobutylene group, a 1-methylpentylene group, a 1-ethylpentylene group, a sec-butylene group, a t-butylene group, an n-pentylene group, an isopentylene group, a neopentylene group, an n-hexylene group, an isohexylene group, an n-heptylene group, an n-octylene group, an n-nonylene group, an n-decylene group, an n-undecylene group, an n-dodecylene group, an n-tridecylene group, an n-tetradecylene group, an n-pentadecylene group, an n-hexadecylene group, an n-heptadecylene group, an n-octadecylene group, an n-nonadecylene group, an n-icosylene group, and the like. The number of carbon atoms of the substituted or unsubstituted alkylene group having 1 to 20 carbon atoms is preferably 1 to 12, and more preferably 4 to 10.

Examples of a substituent that may substitute the substituted or unsubstituted alkylene group having 1 to 20 carbon atoms represented by D include a halogen atom such as a fluorine atom and a chlorine atom; a cyano group; a substituted amino group such as a dimethylamino group; an alkoxy group having 1 to 20 carbon atoms, such as a methoxy group, an ethoxy group, an isopropoxy group, and a butoxy group; an alkoxy group having 1 to 12 carbon atoms that is substituted with an alkoxy group having 1 to 12 carbon atoms, such as a methoxymethoxy group and a methoxyethoxy group; a nitro group; an aryl group such as a phenyl group and a naphthyl group; a cycloalkyl group having 3 to 8 carbon atoms, such as a cyclopropyl group, a cyclopentyl group, and a cyclohexyl group; a cycloalkyloxy group having 3 to 8 carbon atoms, such as a cyclopentyloxy group and a cyclohexyloxy group; a cyclic ether group having 2 to 12 carbon atoms, such as a tetrahydrofuranyl group, a tetrahydropyranyl group, a dioxoranyl group, and a dioxanyl group; an aryloxy group having 6 to 14 carbon atoms, such as a phenoxy group and a naphthoxy group; a fluoroalkoxy group having 1 to 12 carbon atoms in which at least one hydrogen atom is substituted with a fluorine atom, such as a trifluoromethyl group, a pentafluoroethyl group, and

a 2,2,2-trifluoroethyl group; a benzofuryl group; a benzopyranyl group; a benzodioxolyl group; a benzodioxanyl group; —SO₂R⁴; —C(═O)—R⁵; —C(═O)—OR⁵; —SR⁵; an alkoxy group having 1 to 12 carbon atoms that is substituted with —SR⁵; a hydroxyl group; and the like. Note that R⁴ represents an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 2 to 12 carbon atoms, a phenyl group, or a 4-methylphenyl group, and R⁵ represents an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 2 to 12 carbon atoms, a cycloalkyl group having 3 to 12 carbon atoms, or an aromatic hydrocarbon group having 6 to 12 carbon atoms.

Examples of the cycloalkanediyl group having 3 to 20 carbon atoms (that is substituted or unsubstituted) that may be represented by D include a cyclopropanediyl group; a cyclobutanediyl group such as a cyclobutane-1,2-diyl group and a cyclobutane-1,3-diyl group; a cyclopentanediyl group such as a cyclopentane-1,2-diyl group and a cyclopentane-1,3-diyl group; a cyclohexanediyl group such as a cyclohexane-1,2-diyl group, a cyclohexane-1,3-diyl group, and a cyclohexane-1,4-diyl group; a cycloheptanediyl group such as a cycloheptane-1,2-diyl group, a cycloheptane-1,3-diyl group, and a cycloheptane-1,4-diyl group; a cyclooctanediyl group such as a cyclooctane-1,2-diyl group, a cyclooctane-1,3-diyl group, a cyclooctane-1,4-diyl group, and a cyclooctane-1,5-diyl group; a cyclodecanediyl group such as a cyclodecane-1,2-diyl group, a cyclodecane-1,3-diyl group, a cyclodecane-1,4-diyl group, and a cyclodecane-1,5-diyl group; a cyclododecanediyl group such as a cyclododecane-1,2-diyl group, a cyclododecane-1,3-diyl group, a cyclododecane-1,4-diyl group, and a cyclododecane-1,5-diyl group; a cyclotetradecanediyl group such as a cyclotetradecane-1,2-diyl group, a cyclotetradecane-1,3-diyl group, a cyclotetradecane-1,4-diyl group, a cyclotetradecane-1,5-diyl group, and a cyclotetradecane-1,7-diyl group; a cycloeicosanediyl group such as a cycloeicosane-1,2-diyl group and a cycloeicosane-1,10-diyl group; and the like.

The cycloalkanediyl group having 3 to 30 carbon atoms that may be represented by D is classified into a cis-stereoisomer and a trans-stereoisomer that differ in the steric configuration of the carbon atoms bonded to N and Y⁹.

The cycloalkanediyl group may be a cis-isomer, a trans-isomer, or a mixture including a cis-isomer and a trans-isomer.

Examples of a substituent that may substitute the cycloalkanediyl group having 3 to 20 carbon atoms that may be represented by D include a halogen atom such as a fluorine atom and a chlorine atom; a cyano group; a substituted amino group such as a dimethylamino group; an alkyl group having 1 to 6 carbon atoms, such as a methyl group, an ethyl group, and a propyl group; an alkoxy group having 1 to 6 carbon atoms, such as a methoxy group, an ethoxy group, and an isopropoxy group; a nitro group; an aryl group such as a phenyl group and a naphthyl group; a cycloalkyl group having 3 to 8 carbon atoms, such as a cyclopropyl group, a cyclopentyl group, and a cyclohexyl group; —C(═O)—R⁵; —C(═O)—OR⁵; —SO₂R⁴; a hydroxyl group; and the like. Note that R⁴ and R⁵ are the same as defined above.

It is preferable that D be a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, or —C(═O)— (provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded), more preferably a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms, still more preferably an alkylene group having 1 to 20 carbon atoms, and particularly preferably an alkylene group having 1 to 6 carbon atoms.

A¹ represents a substituted or unsubstituted trivalent aromatic group. The trivalent aromatic group may be a trivalent carbocyclic aromatic group, or may be a trivalent heterocyclic aromatic group. It is preferable that the trivalent aromatic group be a trivalent carbocyclic aromatic group, more preferably a trivalent benzene ring group or a trivalent naphthalene ring group, and still more preferably a group among a trivalent benzene ring group and trivalent naphthalene ring groups respectively represented by the following formulas, in order to more advantageously achieve the intended effects of the invention.

Note that the substituents Y¹ and Y² are also included in the following formulas so that the bonding state can be easily understood (Y¹ and Y² are the same as defined above; hereinafter the same).

A¹ is more preferably a group among groups respectively represented by the following formulas (A11) to (A25), still more preferably a group among the groups respectively represented by the formulas (A11), (A13), (A15), (A19), and (A23), and particularly preferably the group represented by the formula (A11) or the group represented by the formula (A23).

Examples of a substituent that may substitute the trivalent aromatic group represented by A¹ include a halogen atom such as a fluorine atom and a chlorine atom; a cyano group; an alkyl group having 1 to 6 carbon atoms, such as a methyl group, an ethyl group, and a propyl group; an alkenyl group having 2 to 6 carbon atoms, such as a vinyl group and an allyl group; an alkyl halide group having 1 to 6 carbon atoms, such as a trifluoromethyl group; a substituted amino group such as a dimethylamino group; an alkoxy group having 1 to 6 carbon atoms, such as a methoxy group, an ethoxy group, and an isopropoxy group; a nitro group; an aryl group such as a phenyl group and a naphthyl group; —C(═O)—R⁶; —C(═O)—OR⁶; —SO₂R⁶; and the like. Note that R⁶ is an alkyl group having 1 to 6 carbon atoms (e.g., methyl group or ethyl group), or an aryl group having 6 to 14 carbon atoms (e.g., phenyl group). It is preferable that A¹ be unsubstituted.

Each of A² and A³ independently represents a substituted or unsubstituted divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms.

Examples of the divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms include a cycloalkanediyl group having 3 to 30 carbon atoms, a divalent fused alicyclic group having 10 to 30 carbon atoms, and the like.

Examples of the cycloalkanediyl group having 3 to 30 carbon atoms include a cyclopropanediyl group; a cyclobutanediyl group such as a cyclobutane-1,2-diyl group and a cyclobutane-1,3-diyl group; a cyclopentanediyl group such as a cyclopentane-1,2-diyl group and a cyclopentane-1,3-diyl group; a cyclohexanediyl group such as a cyclohexane-1,2-diyl group, a cyclohexane-1,3-diyl group, and a cyclohexane-1,4-diyl group; a cycloheptanediyl group such as a cycloheptane-1,2-diyl group, a cycloheptane-1,3-diyl group, and a cycloheptane-1,4-diyl group; a cyclooctanediyl group such as a cyclooctane-1,2-diyl group, a cyclooctane-1,3-diyl group, a cyclooctane-1,4-diyl group, and a cyclooctane-1,5-diyl group; a cyclodecanediyl group such as a cyclodecane-1,2-diyl group, a cyclodecane-1,3-diyl group, a cyclodecane-1,4-diyl group, and a cyclodecane-1,5-diyl group; a cyclododecanediyl group such as a cyclododecane-1,2-diyl group, a cyclododecane-1,3-diyl group, a cyclododecane-1,4-diyl group, and a cyclododecane-1,5-diyl group; a cyclotetradecanediyl group such as a cyclotetradecane-1,2-diyl group, a cyclotetradecane-1,3-diyl group, a cyclotetradecane-1,4-diyl group, a cyclotetradecane-1,5-diyl group, and a cyclotetradecane-1,7-diyl group; a cycloeicosanediyl group such as a cycloeicosane-1,2-diyl group and a cycloeicosane-1,10-diyl group; and the like.

Examples of the divalent fused alicyclic group having 10 to 30 carbon atoms include a decalindiyl group such as a decalin-2,5-diyl group and a decalin-2,7-diyl group; an adamantanediyl group such as an adamantane-1,2-diyl group and an adamantane-1,3-diyl group; a bicyclo[2.2.1]heptanediyl group such as a bicyclo[2.2.1]heptane-2,3-diyl group, a bicyclo[2.2.1]heptane-2, 5-diyl group, and a bicyclo[2.2.1]heptane-2,6-diyl group; and the like.

These divalent alicyclic hydrocarbon groups may be substituted with a substituent at an arbitrary position. Examples of the substituent are the same as those mentioned above in connection with the aromatic group represented by A¹.

A² and A³ are preferably a divalent alicyclic hydrocarbon group having 3 to 12 carbon atoms, more preferably a cycloalkanediyl group having 3 to 12 carbon atoms, still more preferably a group among the groups respectively represented by the following formulas (A31) to (A34), and particularly preferably the group represented by the formula (A32).

The divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms is classified into a cis-stereoisomer and a trans-stereoisomer that differ in the steric configuration of the carbon atoms bonded to Y¹ and Y³ (or Y² and Y⁴). For example, a cyclohexane-1,4-diyl group is classified into a cis-isomer (A32a) and a trans-isomer (A32b) (see below).

The divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms may be a cis-isomer, a trans-isomer, or a mixture including a cis-isomer and a trans-isomer. Note that it is preferable that the divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms be a trans-isomer or a cis-isomer, and more preferably a trans-isomer, since an excellent alignment capability can be obtained.

Each of A⁴ and A⁵ independently represents a substituted or unsubstituted divalent aromatic group having 4 to 30 carbon atoms.

The aromatic group represented by A⁴ and A⁵ may be a monocyclic aromatic group, or may be a polycyclic aromatic group.

Specific examples of a preferable aromatic group represented by A⁴ and A⁵ include the groups respectively represented by the following formulas.

The divalent aromatic group represented by A⁴ and A⁵ may be substituted with a substituent at an arbitrary position.

Examples of the substituent include a halogen atom, a cyano group, a hydroxyl group, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a nitro group, a —C(═O)—OR⁷ group, and the like. Note that R⁷ is an alkyl group having 1 to 6 carbon atoms. Among these, a halogen atom, an alkyl group having 1 to 6 carbon atoms, and an alkoxy group having 1 to 6 carbon atoms are preferable as the substituent. A fluorine atom is preferable as the halogen atom. A methyl group, an ethyl group, and a propyl group are preferable as the alkyl group having 1 to 6 carbon atoms. A methoxy group and an ethoxy group are preferable as the alkoxy group having 1 to 6 carbon atoms.

It is preferable that each of A⁴ and A⁵ be independently a group among the groups respectively represented by the following formulas (A41), (A42), and (A43) that are optionally substituted with a substituent, and particularly preferably the group represented by the formula (A41) that is optionally substituted with a substituent, in order to more advantageously achieve the intended effects of the invention.

Q¹ is a hydrogen atom, or a substituted or unsubstituted alkyl group having 1 to 6 carbon atoms.

Examples of the substituted or unsubstituted alkyl group having 1 to 6 carbon atoms are the same as those mentioned above in connection with R¹.

It is preferable that Q¹ be a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and more preferably a hydrogen atom or a methyl group.

Each of m and n is independently 0 or 1. It is preferable that both m and n be 0.

The polymerizable compound according to one embodiment of the invention may be produced by effecting the following reaction, for example.

wherein Y¹ to Y⁸, G¹, G², Z¹ to Z³, A^(x), D, A¹ to A⁵, Q¹, m, and n are the same as defined above, L is a leaving group (e.g., hydroxyl group, halogen atom, methanesulfonyloxy group, or p-toluenesulfonyloxy group), and —Y^(9a) is a group that reacts with L to form —Y⁹—.

Specifically, the polymerizable compound according to one embodiment of the invention that is represented by the formula (I) can be produced by reacting the hydrazine compound represented by the formula (3) (hydrazine compound (3)) with the carbonyl compound represented by the formula (4) (carbonyl compound (4)) in a molar ratio (hydrazine compound (3):carbonyl compound (4)) of 1:2 to 2:1 (preferably 1:1.5 to 1.5:1) to obtain the compound represented by the formula (II) (compound (II)), and reacting the compound (II) with the compound represented by the formula (5) (compound (5)) in a molar ratio (compound (II):compound (5)) of 1:1 to 1:2 (preferably 1:1.1 to 1:1.5).

The reaction that synthesizes the compound (II) is preferably effected in the presence of an acid catalyst such as an organic acid (e.g., (±)-10-camphorsulfonic acid or p-toluenesulfonic acid), or an inorganic acid (e.g., hydrochloric acid or sulfuric acid). The addition of the acid catalyst may reduce the reaction time, and improve the yield. The acid catalyst is normally added in an amount of 0.001 to 1 mol based on 1 mol of the carbonyl compound (4). The acid catalyst may be added directly, or a solution prepared by dissolving the acid catalyst in an appropriate solvent may be added.

A solvent used for the above reaction is not particularly limited as long as the solvent is inert to the reaction. Examples of the solvent include an alcohol-based solvent such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, sec-butyl alcohol, and t-butyl alcohol; an ether-based solvent such as diethyl ether, tetrahydrofuran, 1,2-dimethoxyethane, 1,4-dioxane, and cyclopentyl methyl ether; an ester-based solvent such as ethyl acetate, propyl acetate, and methyl propionate; an aromatic hydrocarbon-based solvent such as benzene, toluene, and xylene; an aliphatic hydrocarbon-based solvent such as n-pentane, n-hexane, and n-heptane; an amide-based solvent such as N,N-dimethylformamide, N-methylpyrrolidone, and hexamethylphosphoric acid triamide; a sulfur-containing solvent such as dimethyl sulfoxide and sulfolane; a mixed solvent including two or more solvents among these solvents; and the like.

Among these, an alcohol-based solvent, an ether-based solvent, and a mixed solvent including an alcohol-based solvent and an ether-based solvent are preferable.

The solvent may be used in an appropriate amount taking account of the type of each compound, the reaction scale, and the like. The solvent is normally used in an amount of 1 to 100 g per gram of the hydrazine compound (3).

The reaction proceeds smoothly when the reaction temperature is set within the range from −10° C. to the boiling point of the solvent. The reaction time is selected taking account of the reaction scale, but is normally several minutes to several hours.

The compound (II) is then reacted with the compound (5) to obtain the target product.

A combination of the compound (II) and the compound (5) (i.e., a combination of the group -L included in the compound (II) and the group —Y^(9a) included in the compound (5) that take part in the reaction) may be appropriately selected taking account of the target product.

For example, when producing the compound represented by the formula (I) in which —Y⁹— is —O—C(═O)— (compound (Ia)), the reaction is effected using the compound (II) in which L is a hydroxyl group (compound (IIa)) and the compound (5) in which —Y^(9a) is —C(═O)X^(a) (acid halide (5a)). Note that X^(a) is a halogen atom (e.g., chlorine atom or bromine atom).

wherein Y¹ to Y⁸, G¹, G², Z¹ to Z³, A^(x), A¹ to A⁵, Q¹, X^(a), D, m, and n are the same as defined above.

The compound (IIa) and the compound (5a) are preferably reacted in the presence of a base such as triethylamine. The base is normally used in an amount of 1 to 3 mol based on 1 mol of the compound (IIa).

A solvent used for the above reaction is not particularly limited as long as the solvent is inert to the reaction. Examples of the solvent include those mentioned above in connection with the solvent used when reacting the compound (4) and the compound (3).

The hydrazine compound (3) may be produced as described below.

wherein A^(x), D, and L are the same as defined above, and X^(b) represents a leaving group (e.g., halogen atom, methanesulfonyloxy group, or p-toluenesulfonyloxy group).

Specifically the compound represented by the formula (2) (compound (2)) is reacted with the hydrazine compound (1) in an appropriate solvent in a molar ratio (compound (2):compound (1)) of 1:1 to 1:20 (preferably 1:2 to 1:10) to obtain the corresponding hydrazone compound (3).

A solvent used for the above reaction is not particularly limited as long as the solvent is inert to the reaction. Examples of the solvent include an alcohol-based solvent such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, sec-butyl alcohol, and t-butyl alcohol; an ether-based solvent such as diethyl ether, tetrahydrofuran, 1,2-dimethoxyethane, 1,4-dioxane, and cyclopentyl methyl ether; an aromatic hydrocarbon-based solvent such as benzene, toluene, and xylene; an aliphatic hydrocarbon-based solvent such as n-pentane, n-hexane, and n-heptane; an amide-based solvent such as N,N-dimethylformamide, N-methylpyrrolidone, and hexamethylphosphoric acid triamide; a sulfur-containing solvent such as dimethyl sulfoxide and sulfolane; a mixed solvent including two or more solvents among these solvents; and the like.

Among these, an alcohol-based solvent, an ether-based solvent, and a mixed solvent including an alcohol-based solvent and an ether-based solvent are preferable.

The solvent may be used in an appropriate amount taking account of the type of each compound, the reaction scale, and the like. The solvent is normally used in an amount of 1 to 100 g per gram of hydrazine.

The reaction proceeds smoothly when the reaction temperature is set within the range from −10° C. to the boiling point of the solvent. The reaction time is selected taking account of the reaction scale, but is normally several minutes to several hours.

The carbonyl compound (4) may be produced by appropriately bonding and modifying a plurality of known compounds having a desired structure by arbitrarily combining an ether linkage (—O—)-forming reaction, an ester linkage (—C(═O)—O— or —O—C(═O)—)-forming reaction, a carbonate linkage (—O—C(═O)—O—)-forming reaction, and an amide linkage (—C(═O)—NH— or —NH—C(═O)—)-forming reaction.

An ether linkage may be formed as described below.

(i) A compound represented by D1-hal (wherein hal is a halogen atom (hereinafter the same)) and a compound represented by D2-OMet (wherein Met is an alkali metal (mainly sodium) (hereinafter the same)) are mixed and condensed (Williamson synthesis). Note that D1 and D2 are an arbitrary organic group (hereinafter the same). (ii) A compound represented by D1-hal and a compound represented by D2-OH are mixed and condensed in the presence of a base (e.g., sodium hydroxide or potassium hydroxide). (iii) A compound represented by D1-J (wherein J is an epoxy group) and a compound represented by D2-OH are mixed and condensed in the presence of a base (e.g., sodium hydroxide or potassium hydroxide). (iv) A compound represented by D1-OFN (wherein OFN is a group that includes an unsaturated bond) and a compound represented by D2-OMet are mixed and subjected to an addition reaction in the presence of a base (e.g., sodium hydroxide or potassium hydroxide). (v) A compound represented by D1-hal and a compound represented by D2-OMet are mixed and condensed in the presence of copper or cuprous chloride (Ullmann condensation).

An ester linkage and an amide linkage may be formed as described below.

(vi) A compound represented by D1-COOH and a compound represented by D2-OH or D2-NH₂ are subjected to dehydration and condensation in the presence of a dehydration-condensation agent (e.g., N,N-dicyclohexylcarbodiimide). (vii) A compound represented by D1-COOH is reacted with a halogenating agent to obtain a compound represented by D1-CO-hal, and the compound represented by D1-CO-hal is reacted with a compound represented by D2-OH or D2-NH₂ in the presence of a base. (viii) A compound represented by D1-COOH is reacted with an acid anhydride to obtain a mixed acid anhydride, and the mixed acid anhydride is reacted with a compound represented by D2-OH or D2-NH₂. (ix) A compound represented by D1-COOH and a compound represented by D2-OH or D2-NH₂ are subjected to dehydration and condensation in the presence of an acid catalyst or a base catalyst.

More specifically, the carbonyl compound (4) may be produced using the following method (see the following reaction formula).

wherein Y¹ to Y⁸, G¹, G², Z¹, Z², A¹ to A⁵, and Q¹ are the same as defined above, L¹ and L² are a leaving group (e.g., hydroxyl group, halogen atom, methanesulfonyloxy group, or p-toluenesulfonyloxy group), —Y^(1a) is a group that reacts with -L¹ to form —Y¹—, and —Y^(2a) is a group that reacts with -L² to form —Y²—.

Specifically, the carbonyl compound (4) according to one embodiment of the invention may be produced by sequentially reacting the compound represented by the formula (7a) and the compound represented by the formula (7b) with the compound represented by the formula (6d) using an ether linkage (—O—)-forming reaction, an ester linkage (—C(═O)—O— or —O—C(═O)—)-forming reaction, or a carbonate linkage (—O—C(═O)—O—)-forming reaction known in the art.

The carbonyl compound (4) in which Y¹ is a group represented by Y¹¹—C(═O)—O—, and the group represented by Z²—Y⁸-G²-Y⁶-A⁵-(Y⁴-A³)_(n)-Y²— is identical with the group represented by Z¹—Y⁷-G¹-Y⁵-A⁴-(Y³-A²)_(m)-Y¹— (hereinafter referred to as “compound (4′)”) may be produced as shown below.

wherein Y³, Y⁵, Y⁷, G¹, Z¹, A¹, A², A⁴, Q¹, m, and L¹ are the same as defined above, Y¹¹ is a group whereby Y¹ is represented by Y¹¹—C(═O)—O—, and Y¹ is the same as defined above.

Specifically, the dihydroxy compound represented by the formula (6) (compound (6)) is reacted with the compound represented by the formula (7) (compound (7)) in a molar ratio (compound (6):compound (7)) of 1:2 to 1:4 (preferably 1:2 to 1:3) to produce the target compound (4′) with high selectivity in high yield.

When the compound (7) is a compound (carboxylic acid) represented by the formula (7) in which L¹ is a hydroxyl group, the target product may be obtained by effecting the reaction in the presence of a dehydration-condensation agent (e.g., 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride or dicyclohexylcarbodiimide).

The dehydration-condensation agent is normally used in an amount of 1 to 3 mol based on 1 mol of the compound (7).

When the compound (7) is a compound (carboxylic acid) represented by the formula (7) wherein L¹ is a hydroxyl group, the target product may also be obtained by effecting the reaction in the presence of a sulfonyl halide (e.g., methanesulfonyl chloride or p-toluenesulfonyl chloride) and a base (e.g., triethylamine, diisopropylethylamine, pyridine, or 4-(dimethylamino)pyridine).

The sulfonyl halide is normally used in an amount of 1 to 3 mol based on 1 mol of the compound (7).

The base is normally used in an amount of 1 to 3 mol based on 1 mol of the compound (7).

In this case, the compound (mixed acid anhydride) represented by the formula

(7) in which L¹ is a sulfonyloxy group may be isolated, and subjected to the subsequent reaction.

When the compound (7) is a compound (acid halide) represented by the formula (7) in which L¹ is a halogen atom, the target product may be obtained by effecting the reaction in the presence of a base.

Examples of the base include an organic base such as triethylamine and pyridine; and an inorganic base such as sodium hydroxide, sodium carbonate, and sodium hydrogen carbonate.

The base is normally used in an amount of 1 to 3 mol based on 1 mol of the compound (7).

Examples of the solvent used for the above reaction include a chlorine-based solvent such as chloroform and methylene chloride; an amide-based solvent such as N-methylpyrrolidone, N,N-dimethylformamide, N,N-dimethylacetamide, and hexamethylphosphoric triamide; an ether-based solvent such as 1,4-dioxane, cyclopentyl methyl ether, tetrahydrofuran, tetrahydropyran, and 1,3-dioxolane; a sulfur-containing solvent such as dimethyl sulfoxide and sulfolane; an aromatic hydrocarbon-based solvent such as benzene, toluene, and xylene; an aliphatic hydrocarbon-based solvent such as n-pentane, n-hexane, and n-octane; an alicyclic hydrocarbon-based solvent such as cyclopentane and cyclohexane; a mixed solvent including two or more solvents among these solvents; and the like.

The solvent may be used in an appropriate amount taking account of the type of each compound, the reaction scale, and the like. The solvent is normally used in an amount of 1 to 50 g per gram of the hydroxy compound (6).

Many of the compounds (6) are known compounds, and may be produced using a known method.

For example, the compound (6) may be produced using the following method (see the following reaction formula) (see WO2009/042544 and The Journal of Organic Chemistry, 2011, 76, 8082-8087). A commercially available product may be used as the compound (6) either directly or after purification.

wherein A¹ and Q¹ are the same as defined above, A^(1a) is a divalent aromatic group that forms A¹ through formylation or acylation, and R′ is a protecting group for a hydroxyl group, such as an alkyl group having 1 to 6 carbon atoms (e.g., methyl group or ethyl group), or an alkoxyalkyl group having 2 to 6 carbon atoms (e.g., methoxymethyl group).

Specifically, the target compound (6) may be produced by alkylating the hydroxyl groups of the dihydroxy compound represented by the formula (6a) (e.g., 1,4-dihydroxybenzene or 1,4-dihydroxynaphthalene) to obtain the compound represented by the formula (6b), effecting formylation or acylation at the ortho position with respect to the OR′ group using a known method to obtain the compound represented by the formula (6c), and deprotecting (dealkylating) the compound represented by the formula (6c).

A commercially available product may be used as the compound (6) either directly or after purification.

Most of the compounds (7) are known compounds. The compound (7) may be produced by appropriately bonding and modifying a plurality of known compounds having a desired structure by arbitrarily combining an ether linkage (—O—)-forming reaction, an ester linkage (—C(═O)—O— or —O—C(═O)—)-forming reaction, a carbonate linkage (—O—C(═O)—O—)-forming reaction, and an amide linkage (—C(═O)—NH— or —NH—C(═O)—)-forming reaction.

For example, when the compound (7) is a compound represented by the following formula (7′) (compound (7′)), the compound (7) may be produced as shown below using a dicarboxylic acid represented by the formula (9′) (compound (9′)).

wherein Y⁵, Y⁷, G¹, Z¹, A², A⁴, and Y¹¹ are the same as defined above, Y¹² is a group whereby Y³ is represented by —O—C(═O)—Y¹², and R represents an alkyl group (e.g., methyl group or ethyl group) or a substituted or unsubstituted aryl group (e.g., phenyl group or p-methylphenyl group).

Specifically, the sulfonyl chloride represented by the formula (10) is reacted with the compound (9′) in the presence of a base (e.g., triethylamine or 4-(dimethylamino)pyridine).

The compound (8) and a base (e.g., triethylamine or 4-(dimethylamino)pyridine) are added to the reaction mixture to effect a reaction.

Sulfonyl chloride is normally used in an amount of 0.5 to 0.7 equivalents based on 1 equivalent of the compound (9′).

The compound (8) is normally used in an amount of 0.5 to 0.6 equivalents based on 1 equivalent of the compound (9′).

The base is normally used in an amount of 0.5 to 0.7 equivalents based on 1 equivalent of the compound (3).

The reaction temperature is set to 20 to 30° C. The reaction time is determined taking account of the reaction scale and the like, but is normally several minutes to several hours.

Examples of a solvent used for the above reaction include those mentioned above in connection with the solvent that may be used when producing the compound (4′). It is preferable to use an ether as the solvent.

The solvent may be used in an appropriate amount taking account of the type of each compound, the reaction scale, and the like. The solvent is normally used in an amount of 1 to 50 g per gram of the compound (9′).

The target product is isolated by performing a post-treatment operation normally employed in synthetic organic chemistry after completion of the reaction, optionally followed by a known purification/separation means such as column chromatography, recrystallization, or distillation.

The structure of the target product may be identified by measurement/elemental analysis (e.g., NMR spectrometry, IR spectrometry, or mass spectrometry), and the like.

2) Polymerizable Composition

A polymerizable composition according to one embodiment of the invention includes the polymerizable compound according to one embodiment of the invention, and an initiator. The initiator is used to more efficiently polymerize the polymerizable compound according to one embodiment of the invention.

The initiator may be appropriately selected taking account of the type of polymerizable group included in the polymerizable compound. For example, a radical initiator may be used when the polymerizable group is a radically polymerizable group, an anionic initiator may be used when the polymerizable group is an anionically polymerizable group, and a cationic initiator may be used when the polymerizable group is a cationically polymerizable group.

Examples of the radical initiator include a thermal radical generator that is a compound that generates active species that initiate the polymerization of the polymerizable compound upon heating, and a photo-radical generator that is a compound that generates active species that initiate the polymerization of the polymerizable compound upon exposure to exposure light (e.g., visible light, ultraviolet rays (e.g., i-line), deep ultraviolet rays, electron beams, or X-rays). It is preferable to use the photo-radical generator.

Examples of the photo-radical generator include an acetophenone-based compound, a biimidazole-based compound, a triazine-based compound, an O-acyloxime-based compound, an onium salt-based compound, a benzoin-based compound, a benzophenone-based compound, an α-diketone-based compound, a polynuclear quinone-based compound, a xanthone-based compound, a diazo-based compound, an imide sulfonate-based compound, and the like. These compounds generate either or both of active radicals and an active acid upon exposure. These photo-radical generators may be used either alone or in combination.

Specific examples of the acetophenone-based compound include 2-hydroxy-2-methyl-1-phenylpropan-1-one, 2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)butan-1-one, 1-hydroxycyclohexyl phenyl ketone, 2,2-dimethoxy-1,2-diphenylethan-1-one, 1,2-octanedione, 2-benzyl-2-dimethylamino-4′-morpholinobutyrophenone, and the like.

Specific examples of the biimidazole-based compound include 2,2′-bis(2-chlorophenyl)-4,4′,5,5′-tetrakis(4-ethoxycarbonylphenyl)-1,2′-biimidazole, 2,2′-bis(2-bromophenyl)-4,4′,5,5′-tetrakis(4-ethoxycarbonylphenyl)-1,2′-biimidazole, 2,2′-bis(2-chlorophenyl)-4,4′,5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis(2,4-dichlorophenyl)-4,4′,5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis(2,4,6-trichlorophenyl)-4,4′,5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis(2-bromophenyl)-4,4′,5, 5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis(2,4-dibromophenyl)-4,4′,5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis(2,4,6-tribromophenyl)-4,4′,5,5′-tetraphenyl-1,2′-biimidazole, and the like.

When using a biimidazole-based compound as a photoinitiator, it is preferable to use a hydrogen donor in combination with the biimidazole-based compound in order to further improve sensitivity.

The term “hydrogen donor” used herein refers to a compound that can donate a hydrogen atom to radicals generated by the biimidazole-based compound upon exposure. A mercaptan-based compound, an amine-based compound, and the like are preferable as the hydrogen donor.

Examples of the mercaptan-based compound include 2-mercaptobenzothiazole, 2-mercaptobenzoxazole, 2-mercaptobenzimidazole, 2,5-dimercapto-1,3,4-thiadiazole, 2-mercapto-2,5-dimethylaminopyridine, and the like. Examples of the amine-based compound include 4,4′-bis(dimethylamino)benzophenone, 4,4′-bis(diethylamino)benzophenone, 4-diethylaminoacetophenone, 4-dimethylaminopropiophenone, ethyl-4-dimethylaminobenzoate, 4-dimethylaminobenzoic acid, 4-dimethylaminobenzonitrile, and the like.

Specific examples of the triazine-based compound include a triazine-based compound that includes a halomethyl group, such as 2,4,6-tris(trichloromethyl)-s-triazine, 2-methyl-4,6-bis(trichloromethyl)-s-triazine, 2-[2-(5-methylfuran-2-yl)ethenyl]-4,6-bis(trichloromethyl)-s-triazine, 2-[2-(furan-2-yl)ethenyl]-4,6-bis(trichloromethyl)-s-triazine, 2-[2-(4-diethylamino-2-methylphenyl)ethenyl]-4,6-bis(trichloromethyl)-s-triazine, 2-[2-(3,4-dimethoxyphenyl)ethenyl]-4,6-bis(trichloromethyl)-s-triazine, 2-(4-methoxyphenyl)-4,6-bis(trichloromethyl)-s-triazine, 2-(4-ethoxystyryl)-4,6-bis(trichloromethyl)-s-triazine, and 2-(4-n-butoxyphenyl)-4,6-bis(trichloromethyl)-s-triazine.

Specific examples of the O-acyloxime-based compound include 1-[4-(phenylthio)phenyl]-heptane-1,2-dione-2-(O-benzoyloxime), 1-[4-(phenylthio)phenyl]-octane-1,2-dione-2-(O-benzoyloxime), 1-[4-(benzoyl)phenyl]-octane-1,2-dione-2-(O-benzoyloxime), 1-[9-ethyl-6-(2-methylbenzoyl)-9H-carbazol-3-yl]-ethanone-1-(O-acetyloxime), 1-[9-ethyl-6-(3-methylbenzoyl)-9H-carbazol-3-yl]-ethanone-1-(O-acetyloxime), 1-(9-ethyl-6-benzoyl-9H-carbazol-3-yl)-ethanone-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-4-tetrahydrofuranylbenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-4-tetrahydropyranylbenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-5-tetrahydrofuranylbenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-5-tetrahydropyranylbenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-{2-methyl-4-(2,2-dimethyl-1,3-dioxolanyl)benzoyl}-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-4-tetrahydrofuranylmethoxybenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-4-tetrahydropyranylmethoxybenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-5-tetrahydrofuranylmethoxybenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methylbenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-(2-methyl-5-tetrahydropyranylmethoxybenzoyl)-9H-carbazol-3-yl]-1-(O-acetyloxime), ethanone-1-[9-ethyl-6-{2-methyl-4-(2,2-dimethyl-1,3-dioxolanyl)methoxybenzoyl}-9H-carbazol-3-yl]-1-(O-acetyloxime), and the like.

A commercially available product may be used directly as the photo-radical generator. Specific examples of a commercially available product that may be used as the photo-radical generator include Irgacure 907, Irgacure 184, Irgacure 369, Irgacure 651, Irgacure 819, Irgacure 907, and Irgacure OXE02 (manufactured by BASF); Adekaoptomer N1919 (manufactured by Adeka Corporation); and the like.

Examples of the anionic initiator include an alkyllithium compound; a monolithium salt or a monosodium salt of biphenyl, naphthalene, pyrene, and the like; a polyfunctional initiator such as a dilithium salt and a trilithium salt; and the like.

Examples of the cationic initiator include a proton acid such as sulfuric acid, phosphoric acid, perchloric acid, and trifluoromethanesulfonic acid; a Lewis acid such as boron trifluoride, aluminum chloride, titanium tetrachloride, and tin tetrachloride; an aromatic onium salt or a combination of an aromatic onium salt and a reducing agent; and the like.

These initiators may be used either alone or in combination.

The initiator is normally used to prepare the polymerizable composition according to one embodiment of the invention in a ratio of 0.1 to 30 parts by weight, and preferably 0.5 to 10 parts by weight, based on 100 parts by weight of the polymerizable compound.

It is preferable to add a surfactant to the polymerizable composition according to one embodiment of the invention in order to adjust the surface tension of the polymerizable composition. The surfactant is not particularly limited. A nonionic surfactant is normally preferable as the surfactant. A commercially available product may be used as the nonionic surfactant. Examples of a commercially available product that may be used as the nonionic surfactant include an oligomer having a molecular weight of about several thousand (e.g., “KH-40” manufactured by AGC Seimi Chemical Co., Ltd.), and the like. The surfactant is normally added to the polymerizable composition according to one embodiment of the invention in a ratio of 0.01 to 10 parts by weight, and preferably 0.1 to 2 parts by weight, based on 100 parts by weight of the polymerizable compound.

The polymerizable composition according to one embodiment of the invention may further include an additional additive such as an additional copolymerizable monomer (described later), a metal, a metal complex, a dye, a pigment, a fluorescent material, a phosphorescent material, a leveling agent, a thixotropic agent, a gelling agent, a polysaccharide, a UV absorber, an IR (infrared) absorber, an antioxidant, an ion-exchange resin, and a metal oxide (e.g., titanium oxide). Each additive is normally added to the polymerizable composition according to one embodiment of the invention in a ratio of 0.1 to 20 parts by weight based on 100 parts by weight of the polymerizable compound.

The polymerizable composition according to one embodiment of the invention may be prepared by mixing and dissolving given amounts of the polymerizable compound according to one embodiment of the invention, the initiator, and an optional additive in an appropriate organic solvent.

Examples of the organic solvent include a ketone such as cyclopentanone, cyclohexanone, and methyl ethyl ketone; an acetate such as butyl acetate and amyl acetate; a halogenated hydrocarbon such as chloroform, dichloromethane, and dichloroethane; an ether such as 1,4-dioxane, cyclopentyl methyl ether, tetrahydrofuran, tetrahydropyran, and 1,3-dioxolane; and the like.

The polymerizable composition thus obtained is useful as a material for producing a polymer according to one embodiment of the invention, or producing an optically anisotropic product according to one embodiment of the invention (described below).

3) Polymer

A polymer according to one embodiment of the invention is (1) a polymer obtained by polymerizing the polymerizable compound according to one embodiment of the invention, or (2) a polymer obtained by polymerizing the polymerizable composition according to one embodiment of the invention.

The term “polymerization” used herein refers to a chemical reaction in a broad sense including a normal polymerization reaction and a crosslinking reaction.

(1) Polymer Obtained by Polymerizing Polymerizable Compound

The polymer obtained by polymerizing the polymerizable compound according to one embodiment of the invention may be a homopolymer of the polymerizable compound according to one embodiment of the invention, a copolymer of two or more types of the polymerizable compound according to one embodiment of the invention, or a copolymer of the polymerizable compound according to one embodiment of the invention and an additional copolymerizable monomer.

Examples of the additional copolymerizable monomer include a commercially available product such as LC-242 (manufactured by BASF), the compounds disclosed in JP-A-2007-002208, JP-A-2009-173893, JP-A-2009-274984, JP-A-2010-030979, JP-A-2010-031223, JP-A-2011-006360, WO2012/141245, WO2012/147904, WO2012/169424, WO2012/176679, and WO2013/018526, and the like.

Further examples of the additional copolymerizable monomer include 4′-methoxyphenyl 4-(2-methacryloyloxyethyloxy)benzoate, biphenyl 4-(6-methacryloyloxyhexyloxy)benzoate, 4′-cyanobiphenyl 4-(2-acryloyloxyethyloxy)benzoate, 4′-cyanobiphenyl 4-(2-methacryloyloxyethyloxy)benzoate, 3′,4′-difluorophenyl 4-(2-methacryloyloxyethyloxy)benzoate, naphthyl 4-(2-methacryloyloxyethyloxy)benzoate, 4-acryloyloxy-4′-decylbiphenyl, 4-acryloyloxy-4′-cyanobiphenyl, 4-(2-acryloyloxyethyloxy)-4′-cyanobiphenyl, 4-(2-methacryloyloxyethyloxy)-4′-methoxybiphenyl, 4-(2-methacryloyloxyethyloxy)-4′-(4″-fluorobenzyloxy)-biphenyl, 4-acryloyloxy-4′-propylcyclohexylphenyl, 4-methacryloyl-4′-butylbicyclohexyl, 4-acryloyl-4′-amyltolane, 4-acryloyl-4′-(3,4-difluorophenyl)bicyclohexyl, (4-amylphenyl) 4-(2-acryloyloxyethyl)benzoate, (4-(4′-propylcyclohexyl)phenyl) 4-(2-acryloyloxyethyl)benzoate, and the like.

A polyfunctional monomer that includes a plurality of polymerizable unsaturated groups (e.g., acryloyl group, methacryloyl group, vinyl group, and allyl group) may also be used as the additional copolymerizable monomer.

Examples of such a polyfunctional monomer include an alkanediol diacrylate such as 1,2-butanediol diacrylate, 1,3-butanediol diacrylate, 1,4-butanediol diacrylate, neopentanediol diacrylate, and 1,6-hexanediol diacrylate; an alkanediol dimethacrylate such as 1,2-butanediol dimethacrylate, 1,3-butanediol dimethacrylate, 1,4-butanediol dimethacrylate, neopentanediol dimethacrylate, and 1,6-hexanediol dimethacrylate; ethylene glycol diacrylate, and a polyethylene glycol diacrylate such as diethylene glycol diacrylate, triethylene glycol diacrylate, and tetraethylene glycol diacrylate; propylene glycol diacrylate, and a polypropylene glycol diacrylate such as dipropylene glycol diacrylate, tripropylene glycol diacrylate, and tetrapropylene glycol diacrylate; ethylene glycol dimethacrylate, and a polyethylene glycol dimethacrylate such as diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, and tetraethylene glycol dimethacrylate; propylene glycol dimethacrylate, and a polypropylene glycol dimethacrylate such as dipropylene glycol dimethacrylate, tripropylene glycol dimethacrylate, and tetrapropylene glycol dimethacrylate; ethylene glycol divinyl ether, and a polyethylene glycol divinyl ether such as diethylene glycol divinyl ether, triethylene glycol divinyl ether, and tetraethylene glycol divinyl ether; ethylene glycol diallyl ether, and a polyethylene glycol diallyl ether such as diethylene glycol diallyl ether, triethylene glycol diallyl ether, and tetraethylene glycol diallyl ether; bisphenol F ethoxylate diacrylate; bisphenol F ethoxylate dimethacrylate; bisphenol A ethoxylate diacrylate; bisphenol A ethoxylate dimethacrylate; trimethylolpropane triacrylate; trimethylolpropane trimethacrylate; trimethylolpropane ethoxylate triacrylate; trimethylolpropane ethoxylate trimethacrylate; trimethylolpropane propoxylate triacrylate; trimethylolpropane propoxylate trimethacrylate; isocyanuric acid ethoxylate triacrylate; glycerol ethoxylate triacrylate; glycerol propoxylate triacrylate; pentaerythritol ethoxylate tetraacrylate; ditrimethylolpropane ethoxylate tetraacrylate; dipentaerythritol ethoxylate hexacrylate; and the like.

The polymerizable compound according to one embodiment of the invention may be (co)polymerized optionally together with the additional copolymerizable monomer in the presence of an appropriate initiator. The initiator may be used in a ratio similar to that of the initiator included in the polymerizable composition.

When the polymer according to one embodiment of the invention is a copolymer of the polymerizable compound according to one embodiment of the invention and the additional copolymerizable monomer, the content of structural units derived from the polymerizable compound according to one embodiment of the invention is not particularly limited, but is preferably 0.1 to 50 wt %, and more preferably 1 to 40 wt %, based on the total structural units. When the content of structural units derived from the polymerizable compound is within the above range, a polymer that has a high glass transition temperature (Tg) and high hardness can be obtained.

The polymer (1) may be produced by (A) (co)polymerizing the polymerizable compound optionally together with the additional copolymerizable monomer in an appropriate organic solvent in the presence of an appropriate initiator, isolating the target polymer, dissolving the polymer in an appropriate organic solvent to prepare a solution, applying the solution to an appropriate substrate to obtain a film, and drying the film, followed by optional heating, or (B) applying a solution prepared by dissolving the polymerizable compound and an initiator in an organic solvent optionally together with the additional copolymerizable monomer to a substrate using a known coating method, removing the solvent, and effecting polymerization by applying heat or activated energy rays, for example.

Examples of the initiator include those mentioned above in connection with the initiator that is included in the polymerizable composition.

The organic solvent used for polymerization when implementing the method (A) is not particularly limited as long as the organic solvent is inert. Examples of the organic solvent include an aromatic hydrocarbon such as toluene, xylene, and mesitylene; a ketone such as cyclohexanone, cyclopentanone, and methyl ethyl ketone; an acetate such as butyl acetate and amyl acetate; a halogenated hydrocarbon such as chloroform, dichloromethane, and dichloroethane; an ether such as cyclopentyl methyl ether, tetrahydrofuran, and tetrahydropyran; and the like. It is preferable to use a compound having a boiling point of 60 to 250° C., and more preferably 60 to 150° C., from the viewpoint of handling capability.

Examples of the organic solvent used to dissolve the polymer when implementing the method (A), and the organic solvent used for the method (B), include a ketone-based solvent such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclopentanone, and cyclohexanone; an ester-based solvent such as butyl acetate and amyl acetate; a halogenated hydrocarbon-based solvent such as dichloromethane, chloroform, and dichloroethane; an ether-based solvent such as tetrahydrofuran, tetrahydropyran, 1,2-dimethoxyethane, 1,4-dioxane, cyclopentyl methyl ether, and 1,3-dioxolane; an aprotic polar solvent such as N,N-dimethylformamide, N,N-dimethylacetamide, dimethyl sulfoxide, γ-butyrolactone, and N-methylpyrrolidone; and the like. Among these, a compound having a boiling point of 60 to 200° C. is preferable from the viewpoint of handling capability. These solvents may be used either alone or in combination.

A substrate formed of a known organic or inorganic material may be used as the substrate. Examples of the organic material include a polycycloolefin (e.g., Zeonex and Zeonor (registered trademark, manufactured by Zeon Corporation); Arton (registered trademark, manufactured by JSR Corporation); and Apel (registered trademark, manufactured by Mitsui Chemicals Inc.)), polyethylene terephthalate, a polycarbonate, a polyimide, a polyamide, polymethyl methacrylate, polystyrene, polyvinyl chloride, polytetrafluoroethylene, cellulose, cellulose triacetate, polyethersulfone, and the like. Examples of the inorganic material include silicon, glass, calcite, and the like. It is preferable to use a substrate formed of an organic material.

The substrate may be a single-layer substrate, or may be a laminate.

The substrate is preferably a substrate formed of an organic material, and more preferably a resin film that is formed of the organic material.

The polymer solution (method (A)) or the solution subjected to polymerization (method (B)) may be applied to the substrate using a known coating method. Examples of the coating method include a curtain coating method, an extrusion coating method, a roll coating method, a spin coating method, a dip coating method, a bar coating method, a spray coating method, a slide coating method, a print coating method, and the like.

(2) Polymer Obtained by Polymerizing Polymerizable Composition

The polymer according to one embodiment of the invention can be easily obtained by polymerizing the polymerizable composition according to one embodiment of the invention. It is preferable to use the polymerizable composition that includes the initiator (particularly a photoinitiator) in order to more efficiently effect polymerization.

Specifically, it is preferable to produce the polymer according to one embodiment of the invention using the method (B) that applies the polymerizable composition according to one embodiment of the invention to a substrate, and polymerizes the applied polymerizable composition. Examples of the substrate include a substrate used to produce an optically anisotropic product (described later), and the like.

The polymerizable composition according to one embodiment of the invention may be applied to the substrate using a known coating method (e.g., bar coating method, spin coating method, roll coating method, gravure coating method, spray coating method, die coating method, cap coating method, or dipping method). A known organic solvent may be added to the polymerizable composition according to one embodiment of the invention in order to improve the applicability of the polymerizable composition. In this case, it is preferable to remove the organic solvent by natural drying, drying by heating, drying under reduced pressure, drying by heating under reduced pressure, or the like, after applying the polymerizable composition to the substrate.

The polymerizable compound according to one embodiment of the invention or the polymerizable composition according to one embodiment of the invention may be polymerized by applying activated energy rays, or utilizing a thermal polymerization method, for example. It is preferable to polymerize the polymerizable compound or the polymerizable composition by applying activated energy rays since heating is unnecessary (i.e., the reaction can be effected at room temperature). It is preferable to apply light (e.g., ultraviolet rays) to the polymerizable compound or the polymerizable composition since the operation is simple.

The temperature during application of light (irradiation) is preferably set to 30° C. or less. The irradiance is normally set to 1 W/m² to 10 kW/m², and preferably 5 W/m² to 2 kW/m².

A polymer obtained by polymerizing the polymerizable compound according to one embodiment of the invention or the polymerizable composition according to one embodiment of the invention may be removed from the substrate, and used alone, or may be used directly as an organic material of an optical film or the like without removing it from the substrate.

The number average molecular weight of the polymer according to one embodiment of the invention thus obtained is preferably 500 to 500,000, and more preferably 5000 to 300,000. When the number average molecular weight of the polymer is within the above range, the resulting film exhibits high hardness and an excellent handling capability. The number average molecular weight of the polymer may be determined by gel permeation chromatography (GPC) using monodisperse polystyrene as a standard (eluant: tetrahydrofuran).

It is considered that the polymer according to one embodiment of the invention has a structure in which crosslinking points are uniformly present within the molecule. The polymer according to one embodiment of the invention exhibits a high crosslinking efficiency and excellent hardness.

The polymer according to one embodiment of the invention makes it possible to inexpensively produce an optical film that achieves uniform conversion of polarized light over a wide wavelength band, and exhibits satisfactory performance.

4) Optically Anisotropic Product

An optically anisotropic product according to one embodiment of the invention includes (is produced using) the polymer according to one embodiment of the invention.

The optically anisotropic product according to one embodiment of the invention may be obtained by forming an alignment film on a substrate, and forming a polymer film on the alignment film using the polymer according to one embodiment of the invention.

The alignment film is formed on the surface of the substrate in order to achieve the in-plane alignment of an organic semiconductor compound in a single direction.

The alignment film may be obtained by applying a solution (alignment film composition) that includes a polymer (e.g., polyimide, polyvinyl alcohol, polyester, polyallylate, polyamideimide, or polyetherimide) to the substrate to form a film, drying the film, and subjecting the film to a rubbing treatment in one direction, for example.

The thickness of the alignment film is preferably 0.001 to 5 am, and more preferably 0.001 to 1 μm.

The rubbing treatment may be performed on the alignment film or the substrate. The rubbing treatment may be implemented using an arbitrary method. For example, the alignment film may be rubbed in a given direction using a roll around which a cloth or felt formed of synthetic fibers (e.g., nylon) or natural fibers (e.g., cotton) is wound. It is preferable to wash (clean) the alignment film with isopropyl alcohol or the like after completion of the rubbing treatment in order to remove a fine powder (foreign substance) formed during the rubbing treatment, and clean the surface of the alignment film.

The alignment film may be provided with a function of achieving in-plane alignment in a single direction by applying polarized ultraviolet rays to the surface of the alignment film.

A liquid crystal layer may be formed on the alignment film using the polymer according to one embodiment of the invention by utilizing the method described above in connection with the polymer according to one embodiment of the invention.

Since the optically anisotropic product according to one embodiment of the invention is produced using the polymer according to one embodiment of the invention, the optically anisotropic product can be produced at low cost, achieves uniform conversion of polarized light over a wide wavelength band, and exhibits satisfactory performance.

The optically anisotropic product according to one embodiment of the invention may be applied as a retardation film, an alignment film for a liquid crystal display device (liquid crystal display), a polarizer, a viewing angle-improving film, a color filter, a low-pass filter, an optical polarization prism, an optical filter, and the like.

EXAMPLES

The invention is further described below by way of examples. Note that the invention is not limited to the following examples.

Example 1: Synthesis of Compound 1

Step 1: Synthesis of Intermediate A

A four-necked reactor equipped with a thermometer was charged with 8.01 g (105 mmol) of 2-hydrazinoethanol and 30 ml of 2-propanol under a nitrogen stream to prepare a solution. After the addition of 2.00 g (11.8 mmol) of 2-chlorobenzothiazole to the solution, the mixture was refluxed for 3 hours. After completion of the reaction, the reaction mixture was cooled to 25° C., and added to 300 ml of water, followed by extraction with 500 ml of ethyl acetate. The ethyl acetate layer was dried over anhydrous sodium sulfate, and sodium sulfate was filtered off. Ethyl acetate was evaporated from the filtrate under reduced pressure using a rotary evaporator to obtain a white solid. The white solid was recrystallized from ethyl acetate to obtain 0.9 g of an intermediate A (yield: 35.8%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, DMSO-d₆, TMS, δ ppm): 7.66 (dd, 1H, J=1.0 Hz, 8.0 Hz), 7.34 (dd, 1H, J=1.0 Hz, 7.5 Hz), 7.20 (ddd, 1H, J=1.0 Hz, 7.5 Hz, 8.0 Hz), 6.98 (ddd, 1H, J-1.0 Hz, 7.5 Hz, 7.5 Hz), 5.37 (s, 2H), 4.86 (t, 1H, J=5.5 Hz), 3.78 (t, 2H, J=6.5 Hz), 3.72 (dt, 2H, J=5.5 Hz, 6.5 Hz)

Step 2: Synthesis of Intermediate B

A three-necked reactor equipped with a thermometer was charged with 17.98 g (104.42 mmol) of trans-1,4-cyclohexanedicarboxylic acid and 180 ml of tetrahydrofuran (THF) under a nitrogen stream. After the addition of 6.58 g (57.43 mmol) of methanesulfonyl chloride to the mixture, the reactor was immersed in a water bath to adjust the temperature of the reaction mixture to 20° C. 6.34 g (62.65 mmol) of triethylamine (TEA) was added dropwise to the reaction mixture over 10 minutes while maintaining the temperature of the reaction mixture at 20 to 30° C. After the dropwise addition, the mixture was stirred at 25° C. for 2 hours.

After the addition of 0.64 g (5.22 mmol) of 4-(dimethylamino)pyridine and 13.80 g (52.21 mmol) of 4-(6-acryloyloxyhex-1-yloxy)phenol (manufactured by DKSH) to the reaction mixture, the reactor was immersed in a water bath to adjust the temperature of the reaction mixture to 15° C. 6.34 g (62.65 mmol) of TEA was added dropwise to the reaction mixture over 10 minutes while maintaining the temperature of the reaction mixture at 20 to 30° C. After the dropwise addition, the mixture was stirred at 25° C. for 2 hours. After completion of the reaction, 1,000 ml of distilled water and 100 ml of a saturated sodium chloride solution were added to the reaction mixture, followed by extraction twice with 400 ml of ethyl acetate. The organic layer was collected and dried over anhydrous sodium sulfate, and sodium sulfate was filtered off. The solvent was evaporated from the filtrate using a rotary evaporator, and the residue was purified by silica gel column chromatography (THF:toluene=1:9 (volume ratio (hereinafter the same)) to obtain 14.11 g of an intermediate B as a white solid (yield: 65%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, DMSO-d₆, TMS, δ ppm): 12.12 (s, 1H), 6.99 (d, 2H, J=9.0 Hz), 6.92 (d, 2H, J=9.0 Hz), 6.32 (dd, 1H, J=1.5 Hz, 17.5 Hz), 6.17 (dd, 1H, J=10.0 Hz, 17.5 Hz), 5.93 (dd, 1H, J=1.5 Hz, 10.0 Hz), 4.11 (t, 2H, J=6.5 Hz), 3.94 (t, 2H, J=6.5 Hz), 2.48-2.56 (m, 1H), 2.18-2.26 (m, 1H), 2.04-2.10 (m, 2H), 1.93-2.00 (m, 2H), 1.59-1.75 (m, 4H), 1.35-1.52 (m, 8H)

Step 3: Synthesis of Intermediate C

A three-necked reactor equipped with a thermometer was charged with 4.00 g (9.56 mmol) of the intermediate B synthesized in the step 2 and 60 ml of THF under a nitrogen stream to prepare a homogeneous solution. After the addition of 1.12 g (9.78 mmol) of methanesulfonyl chloride to the solution, the reactor was immersed in a water bath to adjust the temperature of the reaction mixture to 20° C. 1.01 g (9.99 mmol) of TEA was added dropwise to the reaction mixture over 5 minutes while maintaining the temperature of the reaction mixture at 20 to 30° C. After the dropwise addition, the mixture was stirred at 25° C. for 2 hours. After the addition of 0.11 g (0.87 mmol) of 4-(dimethylamino)pyridine and 0.60 g (4.35 mmol) of 2,5-dihydroxybenzaldehyde to the reaction mixture, the reactor was immersed in a water bath to adjust the temperature of the reaction mixture to 15° C. 1.10 g (10.87 mmol) of TEA was added dropwise to the reaction mixture over 5 minutes while maintaining the temperature of the reaction mixture at 20 to 30° C. After the dropwise addition, the mixture was stirred at 25° C. for 2 hours. After completion of the reaction, 400 ml of distilled water and 50 ml of a saturated sodium chloride solution were added to the reaction mixture, followed by extraction twice with 750 ml of ethyl acetate. The organic layer was collected and dried over anhydrous sodium sulfate, and sodium sulfate was filtered off. The solvent was evaporated from the filtrate using a rotary evaporator, and the residue was dissolved in 100 ml of THF. 500 ml of methanol was added to the solution to precipitate crystals, which were filtered off. The crystals were washed with methanol, and dried under vacuum to obtain 2.51 g of an intermediate C as a white solid (yield: 62%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, DMSO-d₆, TMS, δ ppm): 10.02 (s, 1H), 7.67 (d, 1H, J=3.0 Hz), 7.55 (dd, 1H, J=3.0 Hz, 8.5 Hz), 7.38 (d, 1H, J=8.5 Hz), 6.99-7.04 (m, 4H), 6.91-6.96 (m, 4H), 6.32 (dd, 2H, J=1.5 Hz, 17.5 Hz), 6.17 (dd, 2H, J=10.0 Hz, 17.5 Hz), 5.93 (dd, 2H, J=1.5 Hz, 10.0 Hz), 4.11 (t, 4H, J=6.5 Hz), 3.95 (t, 4H, J=6.5 Hz), 2.56-2.81 (m, 4H), 2.10-2.26 (m, 8H), 1.50-1.76 (m, 16H), 1.33-1.49 (m, 8H)

Step 4: Synthesis of Intermediate D

A three-necked reactor equipped with a thermometer was charged with 0.760 g (3.64 mmol) of the intermediate A synthesized in the step 1, 3.60 g (3.46 mmol) of the intermediate C synthesized in the step 3, 5 ml of ethanol, and 20 ml of THF under a nitrogen stream to prepare a solution. After the addition of 80.4 mg (0.36 mmol) of (±)-10-camphorsulfonic acid to the solution, the mixture was stirred at 40° C. for 9 hours. After completion of the reaction, 30 ml of ethanol was added to the mixture to precipitate a solid, which was filtered off. The solid was washed with ethanol, and dried using a vacuum dryer to obtain 3.80 g of an intermediate D as a white solid (yield: 97.2%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, CDCl₃, TMS, δ ppm): 7.95 (s, 1H), 7.743-7.73 (m, 1H), 7.69 (dd, 1H, J=0.5 Hz, 7.5 Hz), 7.65 (d, 1H, J=7.5 Hz), 7.35 (ddd, 1H, J=1.0 Hz, 7.0 Hz, 7.5 Hz), 7.19 (ddd, 1H, J=1.0 Hz, 7.5 Hz, 7.5 Hz), 7.119-7.116 (m, 2H), 7.00-6.96 (m, 4H), 6.89-6.87 (m, 4H), 6.40 (dd, 2H, J=1.5 Hz, 17.5 Hz), 6.12 (dd, 2H, J=10.5 Hz, 17.5 Hz), 5.83 (dd, 2H, J=1.5 Hz, 10.5 Hz), 4.45 (t, 2H, J=5.5 Hz), 4.18 (t, 4H, J=8.0 Hz), 4.07-4.02 (m, 2H), 3.946 (t, 2H, J=6.5 Hz), 3.943 (t, 2H, J=6.5 Hz), 2.85-2.80 (br, 1H), 2.73-2.55 (m, 4H), 2.37-2.27 (m, 8H), 1.83-1.65 (m, 16H), 1.55-1.42 (m, 8H)

Step 5: Synthesis of Compound 1

A three-necked reactor equipped with a thermometer was charged with 2.00 g (1.78 mmol) of the intermediate D synthesized in the step 4 and 20 ml of THF under a nitrogen stream to prepare a solution. The solution was cooled to 0° C. After the addition of 240 mg (2.66 mmol) of acryloyl chloride and 358 mg (3.54 mmol) of TEA to the solution, the mixture was stirred at 25° C. for 5 hours. After completion of the reaction, the reaction mixture was added to 50 ml of water, followed by extraction with 200 ml of ethyl acetate. The ethyl acetate layer was dried over anhydrous sodium sulfate, and sodium sulfate was filtered off. Ethyl acetate was evaporated from the filtrate under reduced pressure using a rotary evaporator to obtain a white solid. The white solid was purified by silica gel column chromatography (chloroform:ethyl acetate=95:5) to obtain 1.16 g of a compound 1 as a white solid (yield: 55.2%). The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, CDCl₃, TMS, δ ppm): 8.02 (s, 1H), 7.766-7.760 (m, 1H), 7.70 (dd, 1H, J=0.5 Hz, 8.0 Hz), 7.68 (d, 1H, J=8.0 Hz), 7.36 (ddd, 1H, J=1.0 Hz, 7.5 Hz, 8.0 Hz), 7.19 (ddd, 1H, J=1.0 Hz, 7.5 Hz, 8.0 Hz), 7.12 (d, 2H, J=1.5 Hz), 7.00-6.96 (m, 4H), 6.89-6.87 (m, 4H), 6.41 (dd, 1H, J=1.5 Hz, 17.5 Hz), 6.40 (dd, 2H, J=1.5 Hz, 17.5 Hz), 6.13 (dd, 2H, J=10.5 Hz, 17.5 Hz), 6.10 (dd, 1H, J=10.5 Hz, 17.5 Hz), 5.85 (dd, 1H, J=1.5 Hz, 10.5 Hz), 5.82 (dd, 2H, J=1.5 Hz, 10.5 Hz), 4.59 (t, 2H, J=6.5 Hz), 4.49 (t, 2H, J=6.5 Hz), 4.18 (t, 4H, J=6.5 Hz), 3.95 (t, 4H, J=6.5 Hz), 2.88-2.79 (m, 1H), 2.70-2.56 (m, 3H), 2.38-2.26 (m, 8H), 1.85-1.64 (m, 16H), 1.56-1.42 (m, 8H)

Example 2: Synthesis of Compound 2

Step 1: Synthesis of Intermediate E

A four-necked reactor equipped with a thermometer was charged with 20 g

(144.8 mmol) of 2,5-dihydroxybenzaldehyde, 105.8 g (362.0 mmol) of 4-(6-acryloylhex-1-yloxy)benzoic acid (manufactured by DKSH Japan K.K.), 5.3 g (43.4 mmol) of 4-(dimethylamino)pyridine, and 200 ml of N-methylpyrrolidone under a nitrogen stream to prepare a homogeneous solution. After the addition of 83.3 g (434.4 mol) of 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride (WSC) to the solution, the mixture was stirred at 25° C. for 12 hours. After completion of the reaction, the reaction mixture was added to 1.5 l of water, followed by extraction with 500 ml of ethyl acetate. The ethyl acetate layer was dried over anhydrous sodium sulfate, and sodium sulfate was filtered off. Ethyl acetate was evaporated from the filtrate under reduced pressure using a rotary evaporator to obtain a light yellow solid. The light yellow solid was purified by silica gel column chromatography (toluene:ethyl acetate=9:1) to obtain 75 g of an intermediate E as a white solid (yield: 75.4%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (400 MHz, CDCl₃, TMS, δ ppm): 10.20 (s, 1H), 8.18-8.12 (m, 4H), 7.78 (d, 1H, J=2.8 Hz), 7.52 (dd, 1H, J=2.8 Hz, 8.7 Hz), 7.38 (d, 1H, J=8.7 Hz), 7.00-6.96 (m, 4H), 6.40 (dd, 2H, J=1.4 Hz, 17.4 Hz), 6.12 (dd, 2H, J=10.6 Hz, 17.4 Hz), 5.82 (dd, 2H, J=1.4 Hz, 10.6 Hz), 4.18 (t, 4H, J=6.4 Hz), 4.08-4.04 (m, 4H), 1.88-1.81 (m, 4H), 1.76-1.69 (m, 4H), 1.58-1.42 (m, 8H)

Step 2: Synthesis of Intermediate F

A three-necked reactor equipped with a thermometer was charged with 0.385 g (1.84 mmol) of the intermediate A synthesized in the step 1 of Example 1, 1.20 g (1.75 mmol) of the intermediate E synthesized in the step 2, 3 ml of ethanol, and 15 ml of THF under a nitrogen stream to prepare a solution. After the addition of 40.7 mg (0.17 mmol) of (±)-10-camphorsulfonic acid to the solution, the mixture was stirred at 40° C. for 8 hours. After completion of the reaction, 20 ml of ethanol was added to the mixture to precipitate a solid, which was filtered off. The solid was washed with ethanol, and dried using a vacuum dryer to obtain 1.22 g of an intermediate F as a white solid (yield: 79.2%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, CDCl₃, TMS, δ ppm): 8.20 (d, 2H, J=9.0 Hz), 8.18 (d, 2H, J=9.0 Hz), 8.01 (s, 1H), 7.89 (d, 1H, J=2.5 Hz), 7.62 (d, 1H, J=8.0 Hz), 7.61 (d, 1H, J=8.0 Hz), 7.33-7.28 (m, 3H), 7.15 (ddd, 1H, J=1.0 Hz, 7.5 Hz, 7.5 Hz), 7.09 (d, 4H, J=9.0 Hz), 6.41 (dd, 2H, J=1.5 Hz, 17.5 z), 6.14 (dd, 2H, J=10.5 Hz, 17.5 Hz), 5.84 (dd, 2H, J=1.5 Hz, 10.5 Hz), 4.36 (t, 2H, J=5.5 Hz), 4.194 (t, 2H, J=6.5 Hz), 4.192 (t, 2H, J=6.5 Hz), 4.08 (t, 2H, J=6.5 Hz), 4.07 (t, 2H, J=6.5 Hz), 3.90 (t, 2H, J=5.5 Hz), 3.15 (br, 1H), 1.90-1.84 (m, 4H), 1.77-1.66 (m, 4H), 1.59-1.45 (m, 8H)

Step 3: Synthesis of Compound 2

A three-necked reactor equipped with a thermometer was charged with 1.20 g (1.37 mmol) of the intermediate F synthesized in the step 2 and 15 ml of THF under a nitrogen stream to prepare a solution. The solution was cooled to 0° C. After the addition of 247 mg (2.73 mmol) of acryloyl chloride and 416 mg (4.11 mmol) of TEA to the solution, the mixture was stirred at 25° C. for 2 hours. After completion of the reaction, the reaction mixture was added to 50 ml of water, followed by extraction with 200 ml of ethyl acetate. The ethyl acetate layer was dried over anhydrous sodium sulfate, and sodium sulfate was filtered off. Ethyl acetate was evaporated from the filtrate under reduced pressure using a rotary evaporator to obtain a white solid. The white solid was purified by silica gel column chromatography (chloroform:methanol=97:3) to obtain 1.02 g of a compound 2 as a white solid (yield: 79.9%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, CDCl₃, TMS, δ ppm): 8.21 (d, 2H, J=8.5 Hz), 8.19 (d, 2H, J=8.5 Hz), 8.07 (s, 1H), 7.920-7.915 (m, 1H), 7.64-7.62 (m, 2H), 7.32 (ddd, 1H, J=1.5 Hz, 7.5 Hz, 7.5 Hz), 7.29-7.28 (m, 2H), 7.14 (ddd, 1H, J=1.5 Hz, 7.5 Hz, 7.5 Hz), 7.01 (d, 2H, J=8.5 Hz), 6.99 (d, 2H, J=8.5 Hz), 6.42 (dd, 2H, J=1.5 Hz, 17.5 Hz), 6.21 (dd, 1H, J=1.5 Hz, 17.5 Hz), 6.14 (dd, 2H, J=10.5 Hz, 17.5 Hz), 5.94 (dd, 1H, J=10.5 Hz, 17.5 Hz), 5.83 (dd, 2H, J=1.5 Hz, 10.5 Hz), 5.73 (dd, 1H, J=1.5 Hz, 10.5 Hz), 4.54 (t, 2H, 6.5 Hz), 4.43 (t, 2H, 6.5 Hz), 4.20 (t, 4H, J=6.5 Hz), 4.08 (t, 2H, J=6.5 Hz), 4.07 (t, 2H, J=6.5 Hz), 1.89-1.83 (m, 4H), 1.77-1.72 (m, 4H), 1.59-1.45 (m, 8H)

Comparative Example 1: Synthesis of Compound 1r

Step 1: Synthesis of Intermediate α

A three-necked reactor equipped with a thermometer was charged with 3.00 g (17.69 mmol) of 2-chlorobenzothiazole, 7.65 g (70.74 mmol) of phenylhydrazine, and 30 ml of ethylene glycol under a nitrogen stream to prepare a solution. The solution was heated to 140° C., and reacted for 5 hours. 300 ml of distilled water was added to the reaction mixture, followed by extraction twice with 100 ml of ethyl acetate. The ethyl acetate layer was dried over anhydrous sodium sulfate, and sodium sulfate was filtered off. After concentrating the filtrate using a rotary evaporator, 15 ml of THF was added to the concentrate to prepare a solution. The solution was added to 300 ml of distilled water to precipitate a solid, which was washed with distilled water, and dried under vacuum to obtain a yellow solid. A flask was charged with the yellow solid. After the addition of 50 ml of toluene, the mixture was stirred for 30 minutes, and filtered to remove a toluene-insoluble solid component. The filtrate was concentrated using a rotary evaporator, and the concentrate was purified by silica gel column chromatography (THF:toluene=2:50) to obtain 0.94 g of an intermediate α as a yellow oil (yield: 22%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, DMSO-d₆, TMS, δ ppm): 8.01 (dd, 2H, J=1.0 Hz, 9.0 Hz), 7.78 (dd, 1H, J=1.0 Hz, 8.0 Hz), 7.51 (dd, 1H, J=1.0 Hz, 8.0 Hz), 7.43 (dd, 2H, J=7.5 Hz, 8.5 Hz), 7.28 (dt, 1H, J=1.0 Hz, 7.5 Hz), 7.08-7.16 (m, 2H), 6.26 (s, 2H)

Step 2: Synthesis of Compound 1r

A three-necked reactor equipped with a thermometer was charged with 1.00 g (1.06 mmol) of the intermediate C synthesized in the step 3 of Example 1 and 30 ml of THF under a nitrogen stream to prepare a solution. After the addition of 0.22 ml (0.22 mmol) of 1 N hydrochloric acid and 0.38 g (1.60 mmol) of the intermediate α synthesized in the step 1 to the solution, the mixture was reacted at 40° C. for 2 hours. The reaction mixture was concentrated using a rotary evaporator, and the concentrate was purified by silica gel column chromatography (chloroform:THF=40:1) to obtain 1.14 g of a compound 1r as a light yellow solid (yield: 95%).

The structure of the target product was identified by ¹H-NMR.

¹H-NMR (500 MHz, CDCl₃, TMS, δ ppm): 7.82 (d, 1H, J=2.5 Hz), 7.73 (dd, 1H, J=1.0 Hz, 8.0 Hz), 7.64-7.70 (m, 2H), 7.60 (d, 2H, J=7.5 Hz), 7.35-7.42 (m, 3H), 7.30 (dt, 1H, J=1.0 Hz, 7.5 Hz), 7.18 (dt, 1H, J=1.0 Hz, 7.5 Hz), 7.03-7.12 (m, 2H), 7.00 (d, 2H, J=9.0 Hz), 6.99 (d, 2H, J=9.0 Hz), 6.90 (d, 2H, J=9.0 Hz), 6.89 (d, 2H, J=9.0 Hz), 6.41 (dd, 1H, J=1.5 Hz, 17.5 Hz), 6.41 (dd, 1H, J=1.5 Hz, 17.5 Hz), 6.13 (dd, 1H, J=10.5 Hz, 17.5 Hz), 6.13 (dd, 1H, J=10.5 Hz, 17.5 Hz), 5.82 (dd, 1H, J=1.5 Hz, 10.5 Hz), 5.82 (dd, 1H, J=1.5 Hz, 10.5 Hz), 4.18 (t, 2H, J=6.5 Hz), 4.18 (t, 2H, J=6.5 Hz), 3.92-3.98 (m, 4H), 2.56-2.71 (m, 2H), 2.41-2.50 (m, 1H), 2.27-2.40 (m, 5H), 2.12-2.22 (m, 2H), 1.64-1.91 (m, 14H), 1.41-1.56 (m, 10H), 1.19-1.31 (m, 2H)

The phase transition temperature was measured as described below using the compounds 1 and 2 respectively obtained in Examples 1 and 2, the compound 1r obtained in Comparative Example 1, and the compound 2r (“LC242” manufactured by BASF) of Reference Example 1 that was used in Comparative Example 3.

Measurement of Phase Transition Temperature

10 mg of each compound (compounds 1, 2, 1r, and 2r) was weighed, and placed in a solid state between two glass substrates provided with a polyimide alignment film subjected to a rubbing treatment (manufactured by E.H.C. Co., Ltd.). The substrates were placed on a hot plate, heated from 40° C. to 250° C., and cooled to 40° C. A change in structure during a change in temperature was observed using a polarizing microscope (“ECLIPSE LV100 POL” manufactured by Nikon Corporation).

The phase transition temperature measurement results are shown in Table 1. In Table 1, “C” refers to “crystal”, “N” refers to “nematic”, and “I” refers to “isotropic”. The term “crystal” means that the test compound was in a solid phase, the term “nematic” means that the test compound was in a nematic liquid crystal phase, and the term “isotropic” means that the test compound was in an isotropic liquid phase.

TABLE 1 Example Compound Phase transition temperature Example 1 Compound 1

Example 2 Compound 2

Comparative Example 1 Compound 1r

Reference Example 1 Compound 2r

Example 3

1.0 g of the compound 1 obtained in Example 1, 30 mg of a photoinitiator (“Irgacure 379EG” manufactured by BASF), and 100 mg of a 1% cyclopentanone solution of a surfactant (“KH-40” manufactured by AGC Seimi Chemical Co., Ltd.) were dissolved in 2.3 g of cyclopentanone. The solution was filtered through a disposable filter having a pore size of 0.45 μm to prepare a polymerizable composition 1.

Example 4

A polymerizable composition 2 was prepared in the same manner as in Example 3, except that the compound 2 obtained in Example 2 was used instead of the compound 1.

Comparative Example 2

A polymerizable composition 1r was prepared in the same manner as in Example 3, except that the compound 1r obtained in Comparative Example 1 was used instead of the compound 1.

Comparative Example 3

A polymerizable composition 2r was prepared in the same manner as in Example 3, except that the compound 2r was used instead of the compound 1.

Measurement of Retardation and Evaluation 1 of Wavelength Dispersion (i) Formation of Liquid Crystal Layer Using Polymerizable Composition

Each polymerizable composition (polymerizable compositions 1 to 4) was applied to a transparent glass substrate (provided with a polyimide alignment film subjected to a rubbing treatment) (manufactured by E.H.C. Co., Ltd.) using a #4 wire bar. The resulting film was dried for 1 minute at the temperature shown in Table 2, and subjected to an alignment treatment for 1 minute at the temperature shown in Table 2 to form a liquid crystal layer. Ultraviolet rays were applied (directly) to the liquid crystal layer at a dose of 2,000 mJ/cm² or 2,500 mJ/cm² to effect polymerization to prepare a wavelength dispersion measurement sample.

(ii) Measurement of Retardation

The retardation of the sample between 400 nm and 800 nm was measured using an ellipsometer (“M2000U” manufactured by J. A. Woollam).

(iii) Evaluation of Wavelength Dispersion

The wavelength dispersion was evaluated based on the values α and β that were calculated as described below using the measured retardation.

α=(retardation at 449.9 nm)/(retardation at 548.5 nm)

β=(retardation at 650.2 nm)/(retardation at 548.5 nm)

Table 2 shows the thickness (μm) of each liquid crystal polymer film obtained by polymerizing the polymerizable composition, the retardation (Re) at a wavelength of 548.5 nm, and the values α and β.

Note that the value α is smaller than 1, and the value β is larger than 1 when an ideal wideband wavelength dispersion (reverse wavelength dispersion) is achieved. The values α and β are almost identical to each other when flat wavelength dispersion is achieved. The value α is larger than 1, and the value β is smaller than 1 when normal dispersion is achieved. A flat wavelength dispersion that ensures that the values α and β are almost identical to each other, and a reverse wavelength dispersion that ensures that the value α is smaller than 1, and the value β is larger than 1, are preferable, and the reverse wavelength dispersion that ensures that the value α is smaller than 1, and the value β is larger than 1, is particularly preferable.

TABLE 2 Polymerizable Polymerizable Drying temperature Alignment treatment Dose compound composition (° C.) temperature (° C.) (mJ) Example 3 1  1  120 23 2,000 2,500 Example 4 2  2  100 24 2,000 2,500 Comparative 1r 1r 120 25 2,000 Example 2 2,500 Comparative 2r 2r 80 26 2,000 Example 3 2,500 Change in Thickness Re Wavelength wavelength (μm) (548.5 nm) α β dispersion dispersion Example 3 1.572 134.69 0.906 1.033 Reverse wavelength Did not occur dispersion 1.571 134.55 0.906 1.033 Reverse wavelength dispersion Example 4 1.470 145.26 0.986 0.987 Flat wavelength Did not occur dispersion 1.475 145.33 0.986 0.987 Flat wavelength dispersion Comparative 1.900 148.13 0.879 1.024 Reverse wavelength Occurred Example 2 dispersion 1.500 123.80 0.976 0.989 Flat wavelength dispersion Comparative 1.479 222.90 1.086 0.970 Normal wavelength Did not occur Example 3 dispersion 1.481 223.10 1.087 0.970 Normal wavelength dispersion

The optically anisotropic products of Examples 3 and 4 obtained compounds 1 and 2 showed an ideal reverse wavelength dispersion, and did not show a change in wavelength dispersion depending on the dose of ultraviolet rays.

The optically anisotropic product of Comparative Example 2 obtained using the compound 1r showed reverse wavelength dispersion when the polymerizable composition was polymerized by applying ultraviolet rays at a dose of 2,000 mJ/cm², but showed flat wavelength dispersion when the polymerizable composition was polymerized by applying ultraviolet rays at a dose of 2,500 mJ/cm². Specifically, the optically anisotropic product of Comparative Example 2 showed a change in wavelength dispersion depending on the dose of ultraviolet rays.

The optically anisotropic product of Comparative Example 3 obtained using the compound 2r did not show a change in wavelength dispersion depending on the dose of ultraviolet rays, but showed normal wavelength dispersion.

The embodiments of the invention thus provide a polymerizable compound, a polymerizable composition, and a polymer that have a practical low melting point, exhibit excellent solubility in a general-purpose solvent, can be produced at low cost, and can produce an optical film that achieves uniform conversion of polarized light over a wide wavelength band, and does not show a change in wavelength dispersion even when the dose of ultraviolet rays applied to effect curing is increased, as well as an optically anisotropic product. 

1. A compound represented by a formula (IIa),

wherein each of Y¹ to Y⁸ independently represents a chemical single bond, —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR¹—C(═O)—, —C(═O)—NR¹—, —O—C(═O)—NR¹—, —NR¹—C(═O)—O—, —NR¹—C(═O)—NR¹—, —O—NR¹—, or —NR¹—O—, R¹ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, each of G¹ and G² independently represents a substituted or unsubstituted divalent linear aliphatic group having 1 to 20 carbon atoms, each of Z¹ and Z² independently represents an alkenyl group having 2 to 10 carbon atoms that is substituted with a halogen atom, or unsubstituted, A^(x) represents a group represented by a formula (II),

wherein X represents —NR²—, an oxygen atom, a sulfur atom, and R² represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, provided that an arbitrary C—H is optionally substituted with a nitrogen atom, D represents a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR³—C(═O)—, —C(═O)—NR³—, —NR³—, or —C(═O)—, or a substituted or unsubstituted cycloalkanediyl group having 3 to 20 carbon atoms, provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded, and R³ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, A¹ represents a substituted or unsubstituted trivalent aromatic group, each of A² and A³ independently represents a substituted or unsubstituted divalent alicyclic hydrocarbon group having 3 to 30 carbon atoms, each of A⁴ and A⁵ independently represents a substituted or unsubstituted divalent aromatic group having 4 to 30 carbon atoms, Q¹ represents a hydrogen atom, or a substituted or unsubstituted alkyl group having 1 to 6 carbon atoms, and m and n are independently 0 or
 1. 2. The compound according to claim 1, wherein D is a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, or —C(═O)—, provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded.
 3. The compound according to claim 1, wherein A¹ is a substituted or unsubstituted trivalent benzene ring group, or a substituted or unsubstituted trivalent naphthalene ring group.
 4. The compound according to claim 1, wherein each of Y¹ to Y⁸ is independently a chemical single bond, —O—, —O—C(═O)—, —C(═O)—O—, or —O—C(═O)—O—.
 5. The compound according to claim 1, wherein each of Z¹ and Z² is independently CH₂═CH—, CH₂═C(CH₃)—, or CH₂═C(Cl)—.
 6. The compound according to claim 1, wherein each of G¹ and G² is independently a substituted or unsubstituted divalent aliphatic group having 1 to 12 carbon atoms that optionally includes —O—, —O—C(═O)—, —C(═O)—O—, or —C(═O)—, provided that a case where the aliphatic group includes two or more contiguous —O— is excluded.
 7. The compound according to claim 1, wherein each of G¹ and G² is independently an alkylene group having 1 to 12 carbon atoms.
 8. A method for producing a polymerizable compound comprising reacting the compound according to claim 1 with a precursor compound of said polymerizable compound.
 9. A hydrazine compound represented by a formula (3a),

wherein A^(x) represents a group represented by a formula (II),

wherein X represents —NR²—, an oxygen atom, a sulfur atom, and R² represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, provided that an arbitrary C—H is optionally substituted with a nitrogen atom, D represents a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR³—C(═O)—, —C(═O)—NR³⁻, —NR³—, or —C(═O)—, or a substituted or unsubstituted cycloalkanediyl group having 3 to 20 carbon atoms, provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded, and R³ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms.
 10. The hydrazine compound according to claim 9, wherein D is a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, or —C(═O)—, provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded.
 11. The hydrazine compound according to claim 9, wherein D represents a substituted or unsubstituted alkylene group having 4 to 10 carbon atoms that optionally includes —O—, —S—, —O—C(═O)—, —C(═O)—O—, —O—C(═O)—O—, —NR³—C(═O)—, —C(═O)—NR³—, —NR³—, or —C(═O)—, or a substituted or unsubstituted cycloalkanediyl group having 3 to 20 carbon atoms, provided that a case where the alkylene group includes two or more contiguous —O— or —S— is excluded, and R³ represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms. 